Lack Of Penetration In Friction Stir Welds: Effects On Mechanical Properties And Nde Feasibility
by Nasa Technical Reports Server (ntrs)
2021-06-03 18:05:49
Lack Of Penetration In Friction Stir Welds: Effects On Mechanical Properties And Nde Feasibility
by Nasa Technical Reports Server (ntrs)
2021-06-03 18:05:49
This presentation reviews the issue of lack of penetration (LOP) in Friction Stir Welding and the feasibility of using non-destructive tests to detect . Friction Stir Welding takes place in the solid phase below the melting point of the materials to ...
Read more
This presentation reviews the issue of lack of penetration (LOP) in Friction Stir Welding and the feasibility of using non-destructive tests to detect . Friction Stir Welding takes place in the solid phase below the melting point of the materials to be joined. It thus gives the ability to join materials which are difficult to fusion weld, for example 2000 and 7000 aluminium alloys. This process though can result in a lack of penetration, due to an incomplete penetration of the DXZ. This is frequently referred to as a "kissing bond," which requires micro examination to detect. The presentation then discusses the surface crack tension tests. It then reviews the simulated service test and results. It then discusses the feasibility of using non-destructive examination to detect LOP, the forms of test which can be used, and the results the tests.
Less